Experimental results indicated that the product of hydrolysis was anatase - TiO 2.
結(jié)果表明,水解產(chǎn)物為含水的銳鈦礦型二氧化鈦.
互聯(lián)網(wǎng)
After calcination at 500℃ for 2 h, 0.5 % ( in mole percent ) Pr 3 + - TiO 2 powders show that the nanocrystalline TiO 2 with anatase phase.
樣品經(jīng)500℃焙燒2h后, 0.5% ( 摩爾分?jǐn)?shù),下同 ) Pr3+-TiO2納米粉末為單一的銳鈦型結(jié)構(gòu).
互聯(lián)網(wǎng)
In the case of anatase, higher light powers generated higher photocurrent values at high applied voltages.
對(duì)于銳鈦礦薄膜, 當(dāng)施加較高的外電壓時(shí),越高的光功率會(huì)產(chǎn)生越大的光電流.
互聯(lián)網(wǎng)
TiO 2 film with anatase crystallite and porous structure was available by controlling the preparation conditions.
通過(guò)控制制備條件得到的TiO2薄膜具有銳鈦晶型和多孔性結(jié)構(gòu).